For manufacturers and engineers in Kuwait seeking exceptional corrosion resistance, Nimish Metal in Safat is your trusted source for the Stainless Steel 317L flat bar. We understand that your projects demand materials that can withstand aggressive environments, and our 317L flat bars are specifically formulated to offer superior performance, particularly against chlorides and acids. Sourced with precision, our stock ensures you receive a product that combines durability with the reliability you expect from a leading local supplier.
The strength of 317L lies in its advanced composition, which includes higher levels of molybdenum, chromium, and nickel compared to standard 316 stainless. This specific chemistry grants it excellent resistance to pitting and crevice corrosion. Mechanically, it maintains good tensile strength and yield strength, and it can be easily welded and fabricated. This combination of chemical and physical properties makes it a robust and versatile material for demanding applications.
Standard ASTM A276, A479 / ASME SA276, SA479
Range 3.17 MM TO 350 MM DIA
Diameter 25mm to 152mm
Size Tolerance h8, h9(DIN 671), h10, h11, ASTM A484, DIN 1013
Finish Bright, Polish & Black
Form Round, Square, Hex (A/F), Rectangle, Wire (Coil Form), Wiremesh, Billet, Ingot, Forging Etc.,
Condition Cold Drawn & Polished Cold Drawn, Centreless Ground & Polished
Other Services Machining (CNC), Centreless Grinding (CG), Heat Treatment, Anneling, Pickling, Polish, Rolling, Forging, Cutting, Bending, Minor Fabrication
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 317L | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 – 20.00 | 3.00 – 4.00 | 11.00 – 15.00 | 57.845 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
|---|---|---|---|---|
| 7.9 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | EN |
|---|---|---|---|---|
| SS 317L | 1.4449 | S31700 | SUS 317 | – |
Stainless Steel 317L is primarily composed of iron, with high levels of chromium (18-20%) and nickel (11-15%), along with molybdenum (3-4%) for enhanced corrosion resistance. It also contains small amounts of carbon, manganese, silicon, and phosphorus.
Yes, Stainless Steel 317L Flat Bar is highly resistant to corrosion, especially in harsh environments. Its high chromium, nickel, and molybdenum content enhances resistance to pitting, crevice corrosion, and general oxidation, making it ideal for chemical and marine applications.
Yes, Stainless Steel 317L Flat Bar can be welded easily using standard welding techniques such as TIG, MIG, and SMAW. Its low carbon content minimizes carbide precipitation during welding, ensuring strong joints and excellent corrosion resistance in the weld area.
This flat bar is invaluable in industries where failure is not an option. You will commonly find it in chemical processing equipment, pharmaceutical manufacturing plants, and pollution control scrubbers. Its ability to handle harsh acidic environments also makes it ideal for components in the pulp and paper industry, as well as in flue gas desulfurization systems. Essentially, wherever severe corrosion is a primary concern, the 317L flat bar provides a reliable and long-lasting structural or fabrication solution.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Nimish Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Safat, Kuwait